Extended-life calcium aluminophosphate cement compositions

ABSTRACT

Methods, compositions, and systems for cementing are included. The method comprises providing an extended-life calcium aluminophosphate cement composition comprising calcium aluminate cement, a polyphosphate, water, and a cement set retarder. The method further comprises mixing the extended-life calcium aluminophosphate cement composition with a cement set activator to activate the extended-life calcium aluminophosphate cement composition, introducing the activated extended-life calcium aluminophosphate cement composition into a subterranean formation, and allowing the activated extended-life calcium aluminophosphate cement composition to set in the subterranean formation.

BACKGROUND

Compositions and methods for using extended-life cement compositions in well operations are provided. More particularly, compositions and methods of cementing with extended-life calcium aluminophosphate (“CAP”) cement compositions in well operations are provided.

Cement compositions may be used in a variety of subterranean operations. For example, in subterranean well construction, a pipe string (e.g., casing, liners, expandable tubulars, etc.) may be run into a wellbore and cemented in place. The process of cementing the pipe string in place is commonly referred to as “primary cementing.” In a typical primary cementing method, a cement composition may be pumped into an annulus between the walls of the wellbore and the exterior surface of the pipe string disposed therein. The cement composition may set in the annular space, thereby forming an annular sheath of hardened, substantially impermeable cement (i.e., a cement sheath) that may support and position the pipe string in the wellbore and may bond the exterior surface of the pipe string to the subterranean formation. Among other things, the cement sheath surrounding the pipe string may prevent the migration of fluids in the annulus and may also protect the pipe string from corrosion. Cement compositions may also be used in remedial cementing methods to seal cracks or holes in pipe strings or cement sheaths, to seal highly permeable formation zones or fractures, or to place a cement plug and the like.

A broad variety of cement compositions have been used in subterranean cementing operations. In some instances, extended-life cement compositions have been used. In contrast to conventional cement compositions that set and harden upon preparation, extended-life cement compositions are characterized by being capable of remaining in a pumpable fluid state for at least about one day (e.g., about 7 days, about 2 weeks, about 2 years or more) at room temperature (e.g., about 80° F.) in storage. When desired for use, the extended-life cement compositions should be capable of activation and consequently develop reasonable compressive strengths. For example, an extended-life cement composition that is activated may set into a hardened mass. Among other things, extended-life cement compositions may be suitable for use in wellbore applications such as applications where it is desirable to prepare the cement composition in advance. This may allow the extended-life cement composition to be stored prior to use. In addition, this may allow the extended-life cement composition to be prepared at a convenient location before transportation to the job site. Accordingly, capital expenditures may be reduced due to a reduction in the need for on-site bulk storage and mixing equipment. This may be particularly useful for offshore cementing operations where space onboard the vessels may be limited.

While extended-life cement compositions have been developed heretofore, challenges exist with their successful use in subterranean cementing operations. For example, extended-life cement compositions may have limited use at high temperatures (e.g., temperatures greater than 400° F.) or in corrosive conditions (e.g., subterranean formations comprising carbon dioxide, hydrogen sulfide, etc.). For example, typical extended-life Portland cement compositions may fail at temperatures greater than 230° F. As a further example, both extended-life calcium aluminate cement compositions and extended-life Portland cement compositions may comprise hydroxides, such as calcium hydroxide, either as a component of the composition or as a cement set activator. These hydroxides may be subject to corrosive attacks by carbonic acid (H₂CO₃). Carbonic acid may be naturally present in a subterranean formation, or it may be produced in the subterranean formation by the reaction of subterranean water and carbon dioxide (CO₂), when the latter has been injected into the subterranean formation, e.g., as in a CO₂-enhanced recovery operation. As a result, the permeability of the set cement may increase and chloride and hydrogen sulfide ions, which may be present in the subterranean formation, may penetrate the cement sheath and adversely affect, or react with, the casing. The degradation of the set cement can cause, inter alia, loss of support for the casing and undesirable interzonal communication of fluids.

BRIEF DESCRIPTION OF THE DRAWINGS

These drawings illustrate certain aspects of some of the embodiments of the present method, and should not be used to limit or define the method.

FIG. 1 illustrates a system for preparation and delivery of an extended-life CAP cement composition to a wellbore in accordance with certain examples.

FIG. 2 illustrates surface equipment that may be used in placement of an extended-life CAP cement composition in a wellbore in accordance with certain examples.

FIG. 3 illustrates placement of an extended-life CAP cement composition into a wellbore annulus in accordance with certain examples.

DETAILED DESCRIPTION

Compositions and methods for using extended-life cement compositions in well operations are provided. More particularly, compositions and methods of cementing with extended-life calcium aluminophosphate (“CAP”) cement compositions in well operations are provided.

The extended-life CAP cement compositions may comprise a calcium aluminophosphate cement composition. As used herein, a calcium aluminophosphate cement composition is a composition containing calcium aluminate and a phosphate-containing component that react to form calcium aluminophosphates. The extended-life CAP cement compositions may comprise calcium aluminate cement, a polyphosphate, an aluminosilicate, water, and a cement set retarder. Optionally, the extended-life CAP cement compositions may comprise a cement set activator, a cement set accelerator, and/or a dispersant. Advantageously, the extended-life CAP cement compositions may be capable of remaining in a pumpable fluid state for an extended period of time, i.e., they may be capable of remaining in a pumpable fluid state for at least about one day (e.g., about 7 days, about 2 weeks, about 2 years or more) at room temperature (e.g., about 80° F.) in storage. Generally, the extended-life CAP cement compositions may develop compressive strength after activation. Advantageously, the extended-life CAP cement compositions may develop reasonable compressive strengths at relatively high temperatures (e.g., temperatures above 400° F.). Thus, while the extended-life CAP cement compositions may be suitable for a number of subterranean cementing operations, they may be particularly suitable for use in subterranean formations having relatively high bottom hole static temperatures. Further, the extended-life CAP cement compositions may resist corrosive attacks from corrosive elements, such as carbonic acid or hydrogen sulfide, which may be present in the subterranean formation.

The extended-life CAP cement compositions may comprise a calcium aluminate cement. Any calcium aluminate cement may be suitable for use. Calcium aluminate cements may be described as cements that comprise calcium aluminates in an amount greater than 50% by weight of the dry calcium aluminate cement (i.e., the calcium aluminate cement before water or any additives are added). A calcium aluminate may be defined as any calcium aluminate including, but not limited to, monocalcium aluminate, monocalcium dialuminate, tricalcium aluminate, dodecacalcium hepta-aluminate, monocalcium hexa-aluminate, di calcium aluminate, pentacalcium trialuminate, tetracalcium trialuminate, and the like. One example of a suitable such calcium aluminate is SECAR 71® calcium aluminate, which is commercially available from Kerneos™ Aluminate Technologies. The calcium aluminate cement may be included in the extended-life CAP cement compositions in an amount, without limitation, in the range of from about 10% to about 79% by weight of the extended-life CAP cement compositions. For example, the calcium aluminate cement may be present in an amount ranging between any of and/or including any of about 10%, about 15%, about 20%, about 25%, about 30%, about 35%, about 40%, about 45%, about 50%, about 55%, about 60%, about 65%, about 70%, about 75%, or about 79% by weight of the extended-life CAP cement composition. One of ordinary skill in the art, with the benefit of this disclosure, should be able to choose an appropriate type of calcium aluminate cement and should recognize the appropriate amount of the calcium aluminate cement to include for a chosen application.

The extended-life CAP cement compositions may comprise a polyphosphate. Any polyphosphate-containing compound, phosphate salt, or the like may be sufficient. Examples of polyphosphates may include sodium polyphosphates, such as sodium hexametaphosphate, sodium polytriphosphate; potassium polyphosphates, such as potassium tripolyphosphate, the like, or a combination thereof. A commercial example of a suitable polyphosphate is CALGON® sodium polyphosphate, available from CALGON CARBON CORPORATION®, Pittsburgh, Pa. The polyphosphate may be added to the other components of the extended-life CAP cement composition as an aqueous solution. Alternatively, the polyphosphate may be added to the other components of the extended-life CAP cement composition as a dry solid, or as dry solid particles. The polyphosphate may be included in the extended-life CAP cement compositions in an amount desirable for a particular application as will be evident to those of ordinary skill in the art with the benefit of this disclosure. For example, the polyphosphate may be present in the extended-life CAP cement compositions an amount of about 1% to about 30% by weight of the extended-life CAP cement compositions. For example, the polyphosphate may be present in an amount ranging between any of and/or including any of about 1%, about 5%, about 10%, about 15%, about 20%, about 25%, or about 30% by weight of the extended-life CAP cement composition. One of ordinary skill in the art, with the benefit of this disclosure, should be able to choose an appropriate type of polyphosphate and should recognize the appropriate amount of the polyphosphate to include for a chosen application.

The extended-life CAP cement compositions may comprise a cement set retarder. Examples of the cement set retarder may include, but should not be limited, to hydroxycarboxylic acids such as citric, tartaric, gluconic acids or their respective salts, boric acid or its respective salt, and combinations thereof. A commercial example of a suitable cement set retarder is Fe-2™ Iron Sequestering Agent available from Halliburton Energy Services, Inc., Houston, Tex. Generally, the cement set retarder may be present in the extended-life CAP cement compositions in an amount sufficient to delay the setting for a desired time. The cement set retarder may be present in the extended-life CAP cement compositions in an amount, without limitation, in the range of from about 0.01% to about 10% by weight of the calcium aluminate cement. More particularly, the cement set retarder may be present in an amount ranging between any of and/or including any of about 0.01%, about 0.1%, about 1%, about 2%, about 4%, about 6%, about 8%, or about 10% by weight of the calcium aluminate cement. Additionally, it is important to use cement set retarders that do not undesirably affect the extended-life CAP cement compositions, for example, by increasing the pH of the extended-life CAP cement compositions unless desired. One of ordinary skill in the art, with the benefit of this disclosure, should be able to choose an appropriate type of cement set retarder and should recognize the appropriate amount of the cement set retarder to include for a chosen application.

The extended-life CAP cement compositions may comprise water. The water may be from any source provided that it does not contain an excess of compounds that may undesirably affect other components in the extended-life CAP cement compositions, for example, it may be desirable that no compounds in the water raise the alkalinity of the extended-life CAP cement compositions unless it is desirable to do so. The water may comprise fresh water or salt water. Salt water generally may include one or more dissolved salts therein and may be saturated or unsaturated as desired for a particular application. Seawater or brines may be suitable for use in some applications. Further, the water may be present in an amount sufficient to form a pumpable composition. Without limitation, the water may be present in the extended-life CAP cement compositions in an amount in the range of from about 20% to about 89% by weight of the extended-life CAP cement composition. For example, the water may be present in an amount ranging between any of and/or including any of about 20%, about 25%, about 30%, about 35%, about 40%, 45%, about 50%, about 55%, about 60%, about 65%, about 70%, about 75%, about 80%, about 85%, or about 89% by weight of the extended-life CAP cement composition. One of ordinary skill in the art, with the benefit of this disclosure, should be able to recognize the appropriate amount of water to include for a chosen application.

The extended-life CAP cement compositions may optionally comprise an aluminosilicate. Any aluminosilicate may be sufficient provided it is non-alkaline or possess a component that when mixed with water may raise the alkalinity of the extended-life CAP cement compositions unless it is desirable to do so. For example, Class C fly ash is an aluminosilicate that typically contains a sufficient amount of alkaline material (e.g., lime or hydrated lime) and may raise the alkalinity, and thus induce premature setting of the extended-life CAP cement compositions. Alternatively, Class F fly ash may not typically contain a sufficient amount of an alkaline material such that the alkalinity of the extended-life CAP cement compositions may be raised to a point where premature setting may be induced. Thus, care should be taken when choosing an aluminosilicate so as to not induce premature setting of the extended-life CAP cement composition by undesirably increasing the alkalinity of the extended-life CAP cement composition. Examples of aluminosilicates may include any non-alkaline fly ash, metakaolin, grog, natural pozzolan, vitrified shale, biomass ash (i.e. sugar cane ash, rice husk ash) the like, or a combination thereof. The aluminosilicate may be included in the extended-life CAP cement compositions in an amount desirable for a particular application as will be evident to those of ordinary skill in the art with the benefit of this disclosure. For example, the aluminosilicate may be present in the extended-life CAP cement compositions an amount, without limitation, in a range of about 0% to about 69% by weight of the extended-life CAP cement compositions. For example, the aluminosilicate may be present in an amount ranging between any of and/or including any of about 0%, about 5%, about 10%, about 15%, about 20%, about 25%, about 30%, about 35%, about 40%, about 45%, about 50%, about 55%, about 60%, about 65%, or about 69% by weight of the extended-life CAP cement composition. One of ordinary skill in the art, with the benefit of this disclosure, should be able to choose an appropriate type of aluminosilicate and should recognize the appropriate amount of the aluminosilicate to include for a chosen application.

The extended-life CAP cement compositions may optionally comprise a cement set activator when it is desirable to induce setting of the extended-life CAP cement compositions. Certain cement set activators may additionally function as cement set accelerators and may accelerate the development of compressive strength in the extended-life CAP cement compositions in addition to activating the extended-life CAP cement compositions. A cement set activator may be any alkaline species that increases the pH of the extended-life CAP cement compositions sufficiently to initiate hydration reactions in the extended-life CAP cement compositions, but also does not otherwise interfere with the setting of the extended-life CAP cement compositions. Without being limited by theory, it is believed that activation may be induced due to the cement set activator removing the hydration barrier caused by the cement set retarders in the extended-life CAP cement compositions. Potential examples of cement set activators may include, but should not be limited to: Groups IA and IIA hydroxides such as sodium hydroxide, magnesium hydroxide, and calcium hydroxide; alkaline aluminates such as sodium aluminate; Portland cement, and the like. The cement set activator may be present in the extended-life CAP cement compositions in an amount in the range of from about 0.01% to about 10% by weight of the calcium aluminate cement. More particularly, the cement set activator may be present in an amount ranging between any of and/or including any of about 0.01%, about 0.1%, about 1%, about 2%, about 4%, about 6%, about 8%, or about 10% by weight of the calcium aluminate cement. As discussed above, the cement set activators may comprise calcium hydroxide which may be referred to as hydrated lime. As used herein, the term “hydrated lime” will be understood to mean calcium hydroxide. In some embodiments, the hydrated lime may be provided as quicklime (calcium oxide) which hydrates when mixed with water to form the hydrated lime. The hydrated lime may be included, for example, to activate the extended-life CAP cement compositions.

As discussed above, the cement set activator may comprise a Portland cement. Examples of such Portland cements, include, but are not limited to, Classes A, C, H, or G cements according to the American Petroleum Institute, API Specification for Materials and Testing for Well Cements, API Specification 10, Fifth Ed., Jul. 1, 1990. In addition, the Portland cement may include Portland cements classified as ASTM Type I, II, III, IV, or V.

In some examples, it may be desirable to delay the release of the cement set activator. In such examples, the cement set activator may be combined with a binder. The binder may be used to provide structure for which to hold cement set activator in one or more masses to allow for the cement set activator to be portioned out. Suitable binders may include, but are not limited to, silica gel, aluminosilicate, chitosan, and cellulose, derivatives thereof, and combinations thereof. The amount of binder used is dependent upon the chosen cement set activator and the desired degree to which the chosen cement set activator is to be bound.

The cement set activator and binder may be combined to form a slurry or paste, and then allowed to dry and harden. Once in a hardened form, the cement set activator may be cut or broken into small particles and sized with a sieve. Generally, the particles should have a size that allows for the particles to be transportable into a subterranean formation and mixed with an extended-life CAP cement composition. In some examples, the particles may have a size in a range of about 30 mesh to about 80 mesh. “Mesh” as used herein, refers to US standard size mesh.

Due to the bound nature of this sized-particulate form of the cement set activator, the cement set activator may be released and thus activate the extended-life CAP cement composition at a slower rate relative to a cement set activator that has not been combined with a binder. In some examples, the release of the cement set activator may be further delayed by encapsulating the bound cement set activator with an outer coating (e.g., a degradable coating that degrades downhole) that further impairs the release of the cement set activator. As used herein, the term “coating,” or “outer coating” and the like, does not imply any particular degree of coating on the particulate. In particular, the terms “coat” or “coating” do not imply 100% coverage by the coating on the particulate. In some embodiments, an outer coating, including degree of coating, may be used to control the rate of release of the cement set activator. For example, in a specific example, the outer coating may be configured to impair the release of the cement set activator until the extended-life CAP cement composition is in the portion of the subterranean formation to be cemented, wherein the outer coating may degrade due to elevated temperatures within the subterranean formation and the cement set activator may be released throughout the extended-life CAP cement composition. The time period for delay of the release of the cement set activator may be in a range between any of and/or including any of about 1 minute to about 24 hours. For example, the time period for the delay of release may be in a range between any of and/or including any of about 1 minute, about 5 minutes, about 30 minutes, about 1 hour, about 6 hours, about 12 hours, or about 24 hours. Operation factors such as pump rate, conduit dimensions, and the like may influence the time period for delay.

The outer coating may be formed of a water-insoluble material with a melting point of from about 100° F. to about 500° F. A water insoluble material may prevent the outer coating from dissolving in the extended-life CAP cement compositions until desired. Suitable outer coating materials may include, but should not be limited to, polysaccharides such as dextran and cellulose, chitins, lipids, latex, wax, chitosans, proteins, aliphatic polyesters, poly(lactides), poly(glycolides), poly(ε-caprolactones), poly(hydroxybutyrates), poly(anhydrides), aliphatic polycarbonates, orthoesters, poly(orthoesters), poly(amino acids), poly(ethylene oxides), polyphosphazenes, derivatives thereof, copolymers thereof, or a combination thereof.

As previously mentioned, the extended-life CAP cement compositions may optionally comprise a dispersant. Examples of suitable dispersants may include, without limitation, sulfonated-formaldehyde-based dispersants (e.g., sulfonated acetone formaldehyde condensate), examples of which may include Daxad® 19 dispersant available from Geo Specialty Chemicals, Ambler, Pa. Additionally, polyoxyethylene phosphonates and polyox polycarboxylates may be used. Other suitable dispersants may be polycarboxylated ether dispersants such as Liquiment® 5581F and Liquiment® 514L dispersants available from BASF Corporation Houston, Tex.; or Ethacryl™ G dispersant available from Coatex, Genay, France. An additional example of a suitable commercially available dispersant is CFR™-3 dispersant, available from Halliburton Energy Services, Inc., Houston, Tex. The Liquiment® 514L dispersant may comprise 36% by weight of the polycarboxylated ether in water. While a variety of dispersants may be used, some dispersants may be preferred for use with specific cement set retarders. Additionally, it is may be desired use dispersants that do not undesirably affect the extended-life CAP cement compositions, for example, by inducing premature setting. One of ordinary skill in the art, with the benefit of this disclosure, should recognize the appropriate type of dispersant to include for a chosen application.

The dispersant may be included, without limitation, in the extended-life CAP cement compositions in an amount in the range of from about 0.01% to about 5% by weight of the calcium aluminate cement. More particularly, the dispersant may be present in an amount ranging between any of and/or including any of about 0.01%, about 0.1%, about 0.5%, about 1%, about 2%, about 3%, about 4%, or about 5% by weight of the calcium aluminate cement. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate amount of dispersant to include for a chosen application.

The extended-life CAP cement compositions may optionally comprise a lithium salt which may function as cement set accelerator. A cement set accelerator may accelerate the development of compressive strength once an extended-life CAP cement composition has been activated, but the cement set accelerator, unless otherwise noted, does not itself induce activation of the extended-life CAP cement composition. Examples of suitable lithium salts include, without limitation, lithium sulfate and lithium carbonate. Without being limited by theory, it is believed that the lithium ions increase the number of nucleation sites for hydrate formation in the extended-life CAP cement compositions. Thus, when the extended-life CAP cement compositions are activated by combination with cement set activator, the presence of the lithium salts may accelerate the development of compressive strength of the calcium aluminophosphate cement. Preferably, the lithium salt should be added only to retarded or dormant calcium aluminophosphate cements. Introduction of a lithium salt to a non-retarded or non-dormant calcium aluminophosphate cement may increase the alkalinity of the calcium aluminophosphate cement by a large enough magnitude to induce premature setting of the calcium aluminophosphate cement, based of course, on the specific calcium aluminophosphate cement used and the other components in the composition. However, lithium salts added to retarded or dormant calcium aluminophosphate cements may prevent this risk. The lithium salt may be included in the extended-life CAP cement compositions in an amount, without limitation, in the range of about 0.01% to about 10% by weight of the calcium aluminate cement. More particularly, the lithium salt may be present in an amount ranging between any of and/or including any of about 0.01%, about 0.1%, about 0.5%, about 1%, about 2%, about 3%, about 4%, about 5%, or about 10% by weight of the calcium aluminate cement. One of ordinary skill in the art, with the benefit of this disclosure, should recognize the appropriate amount of lithium salt to include for a chosen application.

Other additives suitable for use in subterranean cementing operations may also be added to the extended-life CAP cement compositions as deemed appropriate by one of ordinary skill in the art. Examples of such additives include, but are not limited to, weighting agents, lightweight additives, gas-generating additives, mechanical property enhancing additives, lost-circulation materials, defoaming agents, foaming agents, thixotropic additives, and combinations thereof. Specific examples of these, and other, additives include salts, fibers, hydratable clays, microspheres, diatomaceous earth, resins, latex, combinations thereof, and the like. Other optional additives may also be included, including, but not limited to, cement kiln dust, lime kiln dust, lime, combinations thereof, and the like. A person having ordinary skill in the art, with the benefit of this disclosure, will be able to determine the type and amount of additive useful for a particular application and desired result.

Weighting agents are typically materials that weigh more than water and may be used to increase the density of the extended-life CAP cement compositions. By way of example, weighting agents may have a specific gravity of about 2 or higher (e.g., about 2, about 4, etc.). Examples of weighting agents that may be used include, but are not limited to, hematite, hausmannite, and barite, and combinations thereof. Specific examples of suitable weighting agents include HI-DENSE® weighting agent, available from Halliburton Energy Services, Inc.

Lightweight additives may be included in the extended-life CAP cement compositions to, for example, decrease the density of the extended-life CAP cement compositions. Examples of suitable lightweight additives include, but are not limited to, bentonite, coal, gilsonite, hollow microspheres, low-density elastic beads, nitrogen, pozzolan-bentonite, sodium silicate, combinations thereof, or other lightweight additives known in the art.

Gas-generating additives may be included in the extended-life CAP cement compositions to release gas at a predetermined time, which may be beneficial to prevent gas migration from the formation through the extended-life CAP cement composition before it hardens. The generated gas may combine with or inhibit the permeation of the extended-life CAP cement composition by formation gas. Examples of suitable gas-generating additives include, but are not limited to, metal particles (e.g., aluminum powder) that react with an alkaline solution to generate a gas.

Mechanical-property-enhancing additives may be included in embodiments of the extended-life CAP cement compositions to, for example, ensure adequate compressive strength and long-term structural integrity. These properties can be affected by the strains, stresses, temperature, pressure, and impact effects from a subterranean environment. Examples of mechanical property enhancing additives include, but are not limited to, carbon fibers, glass fibers, metal fibers, mineral fibers, silica fibers, polymeric elastomers, and latexes.

Lost-circulation materials may be included in embodiments of the extended-life CAP cement compositions to, for example, help prevent the loss of fluid circulation into the subterranean formation. Examples of lost-circulation materials include but are not limited to, cedar bark, shredded cane stalks, mineral fiber, mica flakes, cellophane, calcium carbonate, ground rubber, polymeric materials, pieces of plastic, grounded marble, wood, nut hulls, plastic laminates (Formica® laminate), corncobs, and cotton hulls.

Defoaming additives may be included in the extended-life CAP cement compositions to, for example, reduce the tendency for the extended-life CAP cement compositions to foam during mixing and pumping of the extended-life CAP cement compositions. Examples of suitable defoaming additives include, but are not limited to, polyol silicone compounds. Suitable defoaming additives are available from Halliburton Energy Services, Inc., under the product name D-AIR™ defoamers.

Foaming additives (e.g., foaming surfactants) may be included in the extended-life CAP cement compositions to, for example, facilitate foaming and/or stabilize the resultant foam formed therewith. Examples of suitable foaming additives include, but are not limited to: mixtures of an ammonium salt of an alkyl ether sulfate, a cocoamidopropyl betaine surfactant, a cocoamidopropyl dimethylamine oxide surfactant, sodium chloride, and water; mixtures of an ammonium salt of an alkyl ether sulfate surfactant, a cocoamidopropyl hydroxysultaine surfactant, a cocoamidopropyl dimethylamine oxide surfactant, sodium chloride, and water; hydrolyzed keratin; mixtures of an ethoxylated alcohol ether sulfate surfactant, an alkyl or alkene amidopropyl betaine surfactant, and an alkyl or alkene dimethylamine oxide surfactant; aqueous solutions of an alpha-olefinic sulfonate surfactant and a betaine surfactant; and combinations thereof. An example of a suitable foaming additive is ZONESEALANT™ 2000 agent, available from Halliburton Energy Services, Houston, Tex.

Thixotropic additives may be included in the extended-life CAP cement compositions to, for example, provide an extended-life CAP cement composition that may be pumpable as a thin or low viscosity fluid, but when allowed to remain quiescent attains a relatively high viscosity. Among other things, thixotropic additives may be used to help control free water, create rapid gelation as the composition sets, combat lost circulation, prevent “fallback” in annular column, and minimize gas migration. Examples of suitable thixotropic additives include, but are not limited to, gypsum, water soluble carboxyalkyl, hydroxyalkyl, mixed carboxyalkyl hydroxyalkyl either of cellulose, polyvalent metal salts, zirconium oxychloride with hydroxyethyl cellulose, or a combination thereof.

Those of ordinary skill in the art will appreciate that the extended-life CAP cement compositions generally should have a density suitable for a particular application. By way of example, the extended-life CAP cement compositions may have a density in the range of from about 4 pounds per gallon (“lb/gal”) to about 20 lb/gal. In certain examples, the extended-life CAP cement compositions may have a density in the range of from about 8 lb/gal to about 17 lb/gal. The extended-life CAP cement compositions may be foamed or unfoamed or may comprise other means to reduce their densities, such as hollow microspheres, low-density elastic beads, or other density-reducing additives known in the art. The density may be reduced after storage, but prior to placement in a subterranean formation. Weighting additives may be used to increase the density of the extended-life CAP cement compositions. Examples of suitable weighting additives may include barite, hematite, hausmannite, calcium carbonate, siderite, ilmenite, or combinations thereof. In particular embodiments, the weighting additives may have a specific gravity of 3 or greater. Those of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate density required for a particular application.

As previously mentioned, the extended-life CAP cement compositions may have a delayed set in that they may be capable of remaining in a pumpable fluid state for at least one day (e.g., about 1 day, about 2 weeks, about 2 years or more) at room temperature (e.g., about 80° F.) in storage. For example, the extended-life CAP cement compositions may remain in a pumpable fluid state for a period of time from about 1 day to about 7 days or more. In some embodiments, the extended-life CAP cement compositions may remain in a pumpable fluid state for at least about 1 day, about 7 days, about 10 days, about 20 days, about 30 days, about 40 days, about 50 days, about 60 days, or longer. A fluid is considered to be in a pumpable fluid state where the fluid has a consistency of less than 70 Bearden units of consistency (“Bc”), as measured on a pressurized consistometer in accordance with the procedure for determining cement thickening times set forth in API RP Practice 10B-2, Recommended Practice for Testing Well Cements, First Edition, July 2005.

As discussed above, when desired for use, the extended-life CAP cement compositions may be activated (e.g., by addition of a cement set activator) to set into a hardened mass. The term “activate”, as used herein, refers to the activation of an extended-life CAP cement composition. An extended-life CAP cement composition that has been activated may set to form a hardened mass in a time period in the range of from about 1 hour to about 12 days, without limitation. For example, activated extended-life CAP cement compositions may set to form a hardened mass in a time period ranging between any of and/or including any of about 1 hour, about 6 hours, about 12 hours, about 1 day, about 2 days, about 4 days, about 6 days, about 8 days, about 10 days, about 12 days, or longer.

The extended-life CAP cement compositions may set to have a desirable compressive strength after activation. Compressive strength is generally the capacity of a material or structure to withstand axially directed pushing forces. The compressive strength may be measured at a specified time after the activation of the extended-life CAP cement compositions while the extended-life CAP cement composition is maintained under specified temperature and pressure conditions. Compressive strength can be measured by either destructive or non-destructive methods. The destructive method physically tests the strength of treatment fluid samples at various points in time by crushing the samples in a compression-testing machine. The compressive strength is calculated from the failure load divided by the cross-sectional area resisting the load and is reported in units of pound-force per square inch (psi). Non-destructive methods may employ a UCA™ Ultrasonic Cement Analyzer, available from Fann Instrument Company, Houston, Tex. Compressive strength values may be determined in accordance with API RP 10B-2, Recommended Practice for Testing Well Cements, First Edition, July 2005.

By way of example, extended-life CAP cement compositions that have been activated may develop a 24-hour compressive strength in the range of from about 50 psi to about 5000 psi, alternatively, from about 100 psi to about 4500 psi, or alternatively from about 500 psi to about 4000 psi. In particular, the extended-life CAP cement compositions may develop a compressive strength in 24 hours of at least about 50 psi, at least about 100 psi, at least about 500 psi, or more. The compressive strength values may be determined using destructive or non-destructive methods at any temperature, however compressive strength development at temperatures above 400° F. may be of particular importance for potential use in subterranean formations having relatively high bottom hole static temperatures.

In some examples, the extended-life CAP cement compositions may have desirable thickening times. Thickening time typically refers to the time a fluid, such as an extended-life CAP cement composition, remains in a fluid state capable of being pumped. A number of different laboratory techniques may be used to measure thickening time. A pressurized consistometer, operated in accordance with the procedure set forth in the aforementioned API RP Practice 10B-2, may be used to measure whether a fluid is in a pumpable fluid state. The thickening time may be the time for the treatment fluid to reach 70 Bc and may be reported as the time to reach 70 Bc. The extended-life CAP cement compositions may have thickening times greater than about 1 hour, alternatively, greater than about 2 hours, greater than about 15 hours, greater than about 30 hours, greater than about 100 hours, or alternatively greater than about 190 hours at 3,000 psi and temperatures in a range of from about 50° F. to about 500° F., alternatively, in a range of from about 250° F. to about 500° F., and alternatively at a temperature greater than about 400° F. As will be illustrated in the examples below, thickening times may be controlled by the degree to which the pH of the extended-life CAP cement compositions is increased. This is related, to a degree, to the concentration of the cement set activator and allows for a quantitative method of controlling the set time of the extended-life CAP cement compositions.

As will be appreciated by those of ordinary skill in the art, the extended-life CAP cement compositions may be used in a variety of subterranean operations, including primary and remedial cementing. For example, an extended-life CAP cement composition may be provided that comprises a calcium aluminate cement, a polyphosphate, an aluminosilicate, water, a cement set retarder, and optionally a dispersant, cement set accelerator, and/or a filler material. The cement set activator may be added to the extended-life CAP cement composition to activate the extended-life CAP cement composition prior to being pumped downhole where it may be introduced into a subterranean formation and allowed to set therein. As used herein, introducing the extended-life CAP cement composition into a subterranean formation includes introduction into any portion of the subterranean formation, including, without limitation, into a wellbore drilled into the subterranean formation, into a near wellbore region surrounding the wellbore, or into both.

Additional applications may include storing extended-life CAP cement compositions. For example, an extended-life CAP cement composition may be provided that comprises a calcium aluminate cement, a polyphosphate, an aluminosilicate, water, a cement set retarder, and optionally a dispersant, cement set accelerator, and/or a filler material. The extended-life CAP cement composition may be stored in a vessel or other suitable container. The extended-life CAP cement compositions may be stored and then activated prior to or while pumping downhole. The extended-life CAP cement compositions may be permitted to remain in storage for a desired time period. For example, the extended-life CAP cement compositions may remain in storage for a time period of about 1 day, about 2 weeks, about 2 years, or longer. For example, the extended-life CAP cement compositions may remain in storage for a time period of about 1 day, about 2 days, about 5 days, about 7 days, about 10 days, about 20 days, about 30 days, about 40 days, about 50 days, about 60 days, or up to about 2 years. When desired for use, the extended-life CAP cement compositions may be activated by addition of a cement set activator, introduced into a subterranean formation, and allowed to set therein.

In primary cementing applications, for example, the extended-life CAP cement compositions may be introduced into an annular space between a conduit located in a wellbore and the walls of a wellbore (and/or a larger conduit in the wellbore), wherein the wellbore penetrates the subterranean formation. The extended-life CAP cement compositions may be allowed to set in the annular space to form an annular sheath of hardened cement. The extended-life CAP cement compositions may form a barrier that prevents the migration of fluids in the wellbore. The extended-life CAP cement compositions may also, for example, support the conduit in the wellbore.

In remedial cementing applications, the extended-life CAP cement compositions may be used, for example, in squeeze-cementing operations or in the placement of cement plugs. By way of example, the extended-life compositions may be placed in a wellbore to plug an opening (e.g., a void or crack) in the subterranean formation, in a gravel pack, in the conduit, in the cement sheath, and/or between the cement sheath and the conduit (e.g., a microannulus).

A method for cementing may be provided. The method may be used in conjunction with one or more of the methods, compositions, and/or systems illustrated in FIGS. 1-3. The method may comprise providing an extended-life CAP cement composition comprising calcium aluminate cement, a polyphosphate, water, and a cement set retarder; mixing the extended-life CAP cement composition with a cement set activator to activate the extended-life CAP cement composition; introducing the activated extended-life CAP cement composition into a subterranean formation; and allowing the activated extended-life CAP cement composition to set in the subterranean formation. The cement set retarder may be selected from the group consisting of hydroxycarboxylic acids or their respective salts, boric acid or its respective salt, and any combination thereof. The cement set retarder may be present in an amount of about 0.01% to about 10% by weight of the extended-life CAP cement composition. The polyphosphate may be sodium hexametaphosphate. The polyphosphate may be present in an amount of about 1% to about 30% by weight of the extended-life CAP cement composition. The extended-life CAP cement composition may further comprise an aluminosilicate and the aluminosilicate may be present in an amount of about 1% to about 69% by weight of the extended-life CAP cement composition. The cement set activator may be selected from the group consisting of Groups IA and IIA hydroxides, alkaline aluminates, Portland cement, and the like and the cement set activator may be present in an amount of about 0.01% to about 10% by weight of the extended-life CAP cement composition. The extended-life CAP cement composition may further comprise at least one lithium salt selected from the group consisting of lithium sulfate, lithium carbonate, and any combination thereof. The extended-life CAP cement composition may be stored in a vessel for a time period of at least about 1 day or longer prior to the step of mixing. The extended-life CAP cement composition may be stored in a vessel for a time period of at least about 7 days or longer prior to the step of mixing. The subterranean formation may have a temperature of about 400° F. or more.

An extended-life cementing composition for cementing may be provided. The extended-life cementing composition may be used in conjunction with one or more of the methods, compositions, and/or systems illustrated in FIGS. 1-3. The extended-life cementing composition may comprise calcium aluminate cement, a polyphosphate, water, and a cement set retarder. The cement set retarder may be selected from the group consisting of hydroxycarboxylic acids or their respective salts, boric acid or its respective salt, and any combination thereof. The cement set retarder may be present in an amount of about 0.01% to about 10% by weight of the extended-life CAP cement composition. The polyphosphate may be sodium hexametaphosphate. The polyphosphate may be present in an amount of about 1% to about 30% by weight of the extended-life CAP cement composition. The extended-life CAP cement composition may further comprise an aluminosilicate and the aluminosilicate may be present in an amount of about 1% to about 69% by weight of the extended-life CAP cement composition. The cement set activator may be selected from the group consisting of Groups IA and IIA hydroxides, alkaline aluminates, Portland cement, and the like and the cement set activator may be present in an amount of about 0.01% to about 10% by weight of the extended-life CAP cement composition. The extended-life CAP cement composition may further comprise at least one lithium salt selected from the group consisting of lithium sulfate, lithium carbonate, and any combination thereof.

A system for cementing may be provided. The system may be used in conjunction with one or more of the methods, compositions, and/or systems illustrated in FIGS. 1-3. The system may comprise an extended-life CAP cement composition comprising: calcium aluminate cement, a polyphosphate, water, and a cement set retarder; mixing equipment capable of continuously mixing the extended-life CAP cement composition as it is pumped into a well bore penetrating the subterranean formation; and pumping equipment capable of pumping the extended-life CAP cement composition through a conduit and into a wellbore annulus that is penetrating the subterranean formation. The system may further comprise a vessel capable of storing the extended-life CAP cement composition for a time period of at least about 7 days or longer without setting. The cement set retarder may be selected from the group consisting of hydroxycarboxylic acids or their respective salts, boric acid or its respective salt, and any combination thereof. The cement set retarder may be present in an amount of about 0.01% to about 10% by weight of the extended-life CAP cement composition. The polyphosphate may be sodium hexametaphosphate. The polyphosphate may be present in an amount of about 1% to about 30% by weight of the extended-life CAP cement composition. The extended-life CAP cement composition may further comprise an aluminosilicate and the aluminosilicate may be present in an amount of about 1% to about 69% by weight of the extended-life CAP cement composition. The cement set activator may be selected from the group consisting of Groups IA and IIA hydroxides, alkaline aluminates, Portland cement, and the like and the cement set activator may be present in an amount of about 0.01% to about 10% by weight of the extended-life CAP cement composition. The extended-life CAP cement composition may further comprise at least one lithium salt selected from the group consisting of lithium sulfate, lithium carbonate, and any combination thereof.

Referring now to FIG. 1, preparation of an extended-life CAP cement composition will now be described. FIG. 1 illustrates a system 2 for the preparation of an extended-life CAP cement composition and subsequent delivery of the composition to a wellbore. As shown, the extended-life CAP cement composition may be mixed in mixing equipment 4, such as a jet mixer, re-circulating mixer, or a batch mixer, for example, and then pumped via pumping equipment 6 to the wellbore. The mixing equipment 4 and the pumping equipment 6 may be disposed on one or more cement trucks as will be apparent to those of ordinary skill in the art. A cement set activator may be added to the mixing equipment 4 or may be added to the pumping equipment 6. Alternatively, a cement set activator may be added to an extended-life CAP cement composition after the extended-life CAP cement composition has been pumped into the wellbore. In examples that add a cement set activator to the mixing equipment, a jet mixer may be used, for example, to continuously mix the cement set activator and the extended-life CAP cement composition as it is being pumped to the wellbore. Alternatively, a re-circulating mixer and/or a batch mixer may be used to mix the extended-life CAP cement composition and the cement set activator, and the activator may be added to the mixer as a powder prior to pumping the extended-life CAP cement composition downhole. Additionally, batch mixer type units may be plumbed in line with a separate tank containing a cement set activator. The cement set activator may then be fed in-line with the extended-life CAP cement composition as it is pumped out of the mixing unit. There is no preferred method for preparing or mixing the extended-life CAP cement compositions and one having ordinary skill in the art should be readily able to prepare, mix, and pump the extended-life CAP cement compositions using the equipment on hand.

An example technique for placing an extended-life CAP cement composition into a subterranean formation will now be described with reference to FIGS. 2 and 3. FIG. 2 illustrates surface equipment 10 that may be used in placement of an extended-life CAP cement composition in accordance with certain embodiments. It should be noted that while FIG. 2 generally depicts a land-based operation, those skilled in the art will readily recognize that the principles described herein are equally applicable to subsea operations that employ floating or sea-based platforms and rigs, without departing from the scope of the disclosure. As illustrated by FIG. 2, the surface equipment 10 may include a cementing unit 12, which may include one or more cement trucks. The cementing unit 12 may include the mixing equipment 4 and the pumping equipment 6 shown in FIG. 1 which is represented by system 2 on the cementing unit 12, as will be apparent to those of ordinary skill in the art. The cementing unit 12 may pump an extended-life CAP cement composition 14 through a feed pipe 16 and to a cementing head 18 which conveys the extended-life CAP cement composition 14 downhole.

Turning now to FIG. 3, placing the extended-life CAP cement composition 14 into a subterranean formation 20 will now be described. As illustrated, a wellbore 22 may be drilled into the subterranean formation 20. While wellbore 22 is shown extending generally vertically into the subterranean formation 20, the principles described herein are also applicable to wellbores that extend at an angle through the subterranean formation 20, such as horizontal and slanted wellbores. As illustrated, the wellbore 22 comprises walls 24. In the illustrated embodiment, a surface casing 26 has been inserted into the wellbore 22. The surface casing 26 may be cemented to the walls 24 of the wellbore 22 by cement sheath 28. One or more additional conduits (e.g., intermediate casing, production casing, liners, etc.), shown here as casing 30 may also be disposed in the wellbore 22. As illustrated, there is a wellbore annulus 32 formed between the casing 30 and the walls 24 of the wellbore 22 and/or the surface casing 26. One or more centralizers 34 may be attached to the casing 30, for example, to centralize the casing 30 in the wellbore 22 prior to and during the cementing operation.

With continued reference to FIG. 3, the extended-life CAP cement composition 14 may be pumped down the interior of the casing 30. The extended-life CAP cement composition 14 may be allowed to flow down the interior of the casing 30 through the casing shoe 42 at the bottom of the casing 30 and up around the casing 30 into the wellbore annulus 32. The extended-life CAP cement composition 14 may be allowed to set in the wellbore annulus 32, for example, to form a cement sheath that supports and positions the casing 30 in the wellbore 22. While not illustrated, other techniques may also be utilized for introduction of the extended-life CAP cement composition 14. By way of example, reverse circulation techniques may be used that include introducing the extended-life CAP cement composition 14 into the subterranean formation 20 by way of the wellbore annulus 32 instead of through the casing 30.

As it is introduced, the extended-life CAP cement composition 14 may displace other fluids 36, such as drilling fluids and/or spacer fluids that may be present in the interior of the casing 30 and/or the wellbore annulus 32. At least a portion of the displaced fluids 36 may exit the wellbore annulus 32 via a flow line 38 and be deposited, for example, in one or more retention pits 40 (e.g., a mud pit), as shown on FIG. 2. Referring again to FIG. 3, a bottom plug 44 may be introduced into the wellbore 22 ahead of the extended-life CAP cement composition 14, for example, to separate the extended-life CAP cement composition 14 from the fluids 36 that may be inside the casing 30 prior to cementing. After the bottom plug 44 reaches the landing collar 46, a diaphragm or other suitable device should rupture to allow the extended-life CAP cement composition 14 through the bottom plug 44. In FIG. 3, the bottom plug 44 is shown on the landing collar 46. A top plug 48 may be introduced into the wellbore 22 behind the extended-life CAP cement composition 14. The top plug 48 may separate the extended-life CAP cement composition 14 from a displacement fluid 50 and also push the extended-life CAP cement composition 14 through the bottom plug 44.

The exemplary extended-life CAP cement compositions disclosed herein may directly or indirectly affect one or more components or pieces of equipment associated with the preparation, delivery, recapture, recycling, reuse, and/or disposal of the disclosed extended-life CAP cement compositions. For example, the disclosed extended-life CAP cement compositions may directly or indirectly affect one or more mixers, related mixing equipment, mud pits, storage facilities or units, composition separators, heat exchangers, sensors, gauges, pumps, compressors, and the like used generate, store, monitor, regulate, and/or recondition the exemplary extended-life CAP cement compositions. The disclosed extended-life CAP cement compositions may also directly or indirectly affect any transport or delivery equipment used to convey the extended-life CAP cement compositions to a well site or downhole such as, for example, any transport vessels, conduits, pipelines, trucks, tubulars, and/or pipes used to compositionally move the extended-life CAP cement compositions from one location to another, any pumps, compressors, or motors (e.g., topside or downhole) used to drive the extended-life CAP cement compositions into motion, any valves or related joints used to regulate the pressure or flow rate of the extended-life CAP cement compositions, and any sensors (i.e., pressure and temperature), gauges, and/or combinations thereof, and the like. The disclosed extended-life CAP cement compositions may also directly or indirectly affect the various downhole equipment and tools that may come into contact with the extended-life CAP cement compositions such as, but not limited to, wellbore casing, wellbore liner, completion string, insert strings, drill string, coiled tubing, slickline, wireline, drill pipe, drill collars, mud motors, downhole motors and/or pumps, cement pumps, surface-mounted motors and/or pumps, centralizers, turbolizers, scratchers, floats (e.g., shoes, collars, valves, etc.), logging tools and related telemetry equipment, actuators (e.g., electromechanical devices, hydromechanical devices, etc.), sliding sleeves, production sleeves, plugs, screens, filters, flow control devices (e.g., inflow control devices, autonomous inflow control devices, outflow control devices, etc.), couplings (e.g., electro-hydraulic wet connect, dry connect, inductive coupler, etc.), control lines (e.g., electrical, fiber optic, hydraulic, etc.), surveillance lines, drill bits and reamers, sensors or distributed sensors, downhole heat exchangers, valves and corresponding actuation devices, tool seals, packers, cement plugs, bridge plugs, and other wellbore isolation devices, or components, and the like.

EXAMPLES

To facilitate a better understanding of the present claims, the following examples of certain aspects of the disclosure are given. In no way should the following examples be read to limit, or define, the entire scope of the claims.

Example 1

A comparative experiment was performed using an extended-life calcium aluminate cement composition (Sample 1) and an extended-life CAP cement composition (Sample 2). The calcium aluminate cement composition comprised about 40% to about 70% calcium aluminate cement by weight, about 33% to about 200% water by weight of the calcium aluminate cement, about 0.01% to about 10% cement set retarder by weight of the calcium aluminate cement, and about 0.01% to about 5% dispersant by weight of the calcium aluminate cement. The calcium aluminate cement slurry was obtained from Kerneos, Inc., Chesapeake, Va.; as a retarded calcium aluminate system comprising a suspension of calcium aluminate cement that was 40-70% solids. The calculated density of the calcium aluminate cement composition was 14.7 lb/gal.

The extended-life CAP cement composition comprised 37.6% of the calcium aluminate cement (210 g) by weight of the total cement composition, 4.0% polyphosphate (22.1 g of sodium hexametaphosphate) by weight of the total cement composition, 37.6% aluminosilicate (210 g of Class F fly ash) by weight of the total cement composition, and 20.9% water (117 g). The total composition was 559.1 g and had a density of 15.2 lb/gal.

The apparent viscosities, plastic viscosities, and yield points were calculated from FYSA decay readings of the two compositions as measured over a 14 day period using a Model 35A Fann® Viscometer and a No. 2 spring with a Fann® Yield Stress Adapter (FYSA), in accordance with the procedure set forth in API RP Practice 10B-2, Recommended Practice for Testing Well Cements. The data is presented in Table 1 below.

TABLE 1 Comparative Example of Rheological Profile of Two Extended-life CAP cement compositions Slurry Age (Days) 0 2 4 7 9 11 14 Sample 1 Apparent Viscosity @ 100 RPM 1061 1115 1088 1088 1088 1088 1088 Sample 2 Apparent Viscosity @ 100 RPM 1428 1877 2026 2040 2080 2149 2258 Sample 1 Plastic Viscosity 18 20 21 21 20 21 20 Sample 2 Plastic Viscosity 53 74 75 77 78 79 80 Sample 1 Yield Point 39 41 40 40 40 40 40 Sample 2 Yield Point 52.5 69 74.5 75 76.5 79 83

The data indicate that the extended-life calcium aluminophosphate composition was stable over the 14 day period and exhibited a rheological profile similar to that of the extended-life calcium aluminate cement composition.

Example 2

A 4M solution of sodium hydroxide was added to the calcium aluminophosphate cement composition of Example 1 (Sample 2) to activate it. The sodium hydroxide solution was added at a concentration of 2% by weight of the total composition.

The non-destructive compressive strength was measured using a UCA™ Ultrasonic Cement Analyzer, available from Fann® Instrument Company, Houston, Tex. Compressive strength values may be determined in accordance with API RP 10B-2, Recommended Practice for Testing Well Cements, First Edition, July 2005*. Compressive strength measurements were taken at 12 and 24 hours. Additionally, the time to 50 psi and the time to 500 psi is noted as illustrated in Table 2.

The sample was also subjected to destructive compressive strength (Crush C.S.) testing at 24 hours using a Tinius Olsen mechanical press in accordance with API RP Practice 10B-2, Recommended Practice for Testing Well Cements. The reported compressive strength is an average for two cylinders of each sample. The data is illustrated in Table 2.

TABLE 2 Extended-life CAP cement composition Compressive Strength Measurements 50 psi (hr:mm) 00:30 500 psi (hr:mm) 03:42 12 hr. UCA CS (psi) 1050 24 hr. UCA CS (psi) 1808 24 hr. Crush CS (psi) 1723 *Test Conditions: 100° F., 3000 psi, 15 minute ramp time

The data indicates that the extended-life calcium aluminophosphate cement slurry rapidly builds compressive strength even at temperatures as low as 100° F.

Example 3

A comparative experiment was performed using the extended-life CAP cement composition (Sample 1) from Example 1.

A new extended-life CAP cement composition (Sample 3) was prepared. Sample 3 differs from the extended-life calcium aluminophosphate cement (Sample 2) in Example 1 in that it does not comprise an aluminosilicate. Sample 3 comprised 67.5% calcium aluminate cement (210 g) by weight of the total cement composition, 3.6% polyphosphate (11.05 g of sodium hexametaphosphate) by weight of the total cement composition, and 28.9% water (90 g). The total composition was 311.05 g and had a density of 15.0 lb/gal. The apparent viscosity was calculated from FYSA decay readings of the two slurries as measured over a 10 second period using a Model 35A Fann® Viscometer and a No. 2 spring with a Fann® Yield Stress Adapter (FYSA), in accordance with the procedure set forth in API RP Practice 10B-2, Recommended Practice for Testing Well Cements. The data is presented in Table 3 below.

TABLE 3 Comparative Example of Apparent Viscosity of Two Extended-life CAP cement compositions RPM 3 6 100 200 300 600 Sample 1 Apparent 13147 8160 1088 687 539 408 Viscosity Sample 3 Apparent 9520 5667 802 530 431 354 Viscosity

The data indicate that the extended-life CAP cement composition exhibited an acceptable apparent viscosity for pumping and working. Also it was noted that the extended-life CAP cement composition had a lower apparent viscosity, particularly at lower shear rates, relative to that of the extended-life calcium aluminate cement composition.

Example 4

A 4M solution of sodium hydroxide was added to the extended-life CAP cement composition of Example 3 (Sample 3) to activate it. The sodium hydroxide solution was added at a concentration of 2% by weight of the total composition. Another sample was prepared (Sample 4) which was identical to Sample 3 except a lithium salt (lithium sulfate monohydrate) was added to Sample 4 as a cement set accelerator. The cement set accelerator was added at a concentration of 1% by weight of the total composition. Sample 4 was also activated identically to Sample 3.

The non-destructive compressive strengths of both samples were measured using a UCA™ Ultrasonic Cement Analyzer, available from Fann® Instrument Company, Houston, Tex. Compressive strength values may be determined in accordance with API RP 10B-2, Recommended Practice for Testing Well Cements, First Edition, July 2005*. Compressive strength measurements were taken at 12 and 24 hours. Additionally, the time to 50 psi and the time to 500 psi is noted as illustrated in Table 4.

The samples were also subjected to destructive compressive strength (Crush C.S.) testing at 7 days using a Tinius Olsen mechanical press in accordance with API RP Practice 10B-2, Recommended Practice for Testing Well Cements. The reported compressive strength is an average for two cylinders of each sample. The data is illustrated in Table 4.

TABLE 4 Extended-life CAP cement compositions Compressive Strength Measurements Sample 3 Sample 4 50 psi (hh:mm) 08:11 02:06 500 psi (hh:mm) 50:18 07:40 12 hr. UCA CS (psi) 61 627 24 hr. UCA CS (psi) 176 810 7 day Crush CS (psi) 2223 2151 *Test Conditions: 100° F., 3000 psi, 15 minute ramp time

The data indicates that the extended-life CAP cement compositions build sufficient compressive strength at 7 days even in low temperatures. The data also shows that the addition of a lithium salt increases early strength development.

Example 5

A new extended-life CAP cement composition was prepared (Sample 5) for testing at high temperatures (500° F.). Sample 5 comprised 36.7% calcium aluminate cement (210 g) by weight of the total cement composition, 3.9% polyphosphate (22.1 g of sodium hexametaphosphate) by weight of the total cement composition, 36.7% aluminosilicate (210 g of Class F fly ash) by weight of the total cement composition, and 22.7% water (130 g). The total composition was 572.1 g and had a density of 15.0 ppg.

A 4 M solution of sodium hydroxide was added to Sample 5 to activate it. The sodium hydroxide solution was added at a concentration of 2% by weight of the total composition.

The non-destructive compressive strength was measured using a UCA™ Ultrasonic Cement Analyzer, available from Fann® Instrument Company, Houston, Tex. Compressive strength values may be determined in accordance with API RP 10B-2, Recommended Practice for Testing Well Cements, First Edition, July 2005*. Compressive strength measurements were taken at 12 hours, 24 hours, 48 hours, 72 hours, and 7 days. Additionally, the time to 50 psi and the time to 500 psi was noted as illustrated in Table 5.

TABLE 5 Extended-life CAP cement composition Compressive Strength Measurements 50 psi (hh:mm) 00:42 500 psi (hh:mm) 01:14 12 hr. UCA CS (psi) 3229 24 hr. UCA CS (psi) 2825 48 hr. UCA CS (psi) 2859 72 hr. UCA CS (psi) 2952 7 day UCA CS (psi) 2830 *Test Conditions: 500° F., 3000 psi, 180 minute ramp time

The data indicates that the extended-life calcium aluminophosphate cement was able to maintain a stable compressive strength even at extremely high temperatures.

The preceding description provides various embodiments of the systems and methods of use disclosed herein which may contain different method steps and alternative combinations of components. It should be understood that, although individual embodiments may be discussed herein, the present disclosure covers all combinations of the disclosed embodiments, including, without limitation, the different component combinations, method step combinations, and properties of the system. It should be understood that the compositions and methods are described in terms of “comprising,” “containing,” or “including” various components or steps, the compositions and methods can also “consist essentially of” or “consist of” the various components and steps. Moreover, the indefinite articles “a” or “an,” as used in the claims, are defined herein to mean one or more than one of the element that it introduces.

For the sake of brevity, only certain ranges are explicitly disclosed herein. However, ranges from any lower limit may be combined with any upper limit to recite a range not explicitly recited, as well as, ranges from any lower limit may be combined with any other lower limit to recite a range not explicitly recited, in the same way, ranges from any upper limit may be combined with any other upper limit to recite a range not explicitly recited. Additionally, whenever a numerical range with a lower limit and an upper limit is disclosed, any number and any included range falling within the range are specifically disclosed. In particular, every range of values (of the form, “from about a to about b,” or, equivalently, “from approximately a to b,” or, equivalently, “from approximately a-b”) disclosed herein is to be understood to set forth every number and range encompassed within the broader range of values even if not explicitly recited. Thus, every point or individual value may serve as its own lower or upper limit combined with any other point or individual value or any other lower or upper limit, to recite a range not explicitly recited.

Therefore, the present embodiments are well adapted to attain the ends and advantages mentioned as well as those that are inherent therein. The particular embodiments disclosed above are illustrative only, and may be modified and practiced in different but equivalent manners apparent to those skilled in the art having the benefit of the teachings herein. Although individual embodiments are discussed, the disclosure covers all combinations of all of the embodiments. Furthermore, no limitations are intended to the details of construction or design herein shown, other than as described in the claims below. Also, the terms in the claims have their plain, ordinary meaning unless otherwise explicitly and clearly defined by the patentee. It is therefore evident that the particular illustrative embodiments disclosed above may be altered or modified and all such variations are considered within the scope and spirit of those embodiments. If there is any conflict in the usages of a word or term in this specification and one or more patent(s) or other documents that may be incorporated herein by reference, the definitions that are consistent with this specification should be adopted. 

What is claimed is:
 1. A method of cementing comprising: providing an extended-life calcium aluminophosphate cement composition comprising: a calcium aluminate cement, wherein the calcium aluminate cement is present in an amount of about 40% to about 70% by weight of the extended-life calcium aluminophosphate cement composition; a polyphosphate; water; a cement set retarder, wherein the cement set retarder is present in an amount of about 6% to about 10% by weight of the extended-life calcium aluminophosphate cement composition; aluminosilicate, wherein the aluminosilicate is present in an amount of about 1% to about 69% by weight of the extended-life calcium aluminophosphate cement composition; and sodium hydroxide, and wherein the extended-life calcium aluminophosphate cement composition is free of cement kiln dust; storing the extended life cement composition in a vessel for a time period of at least about 1 day or longer; thereafter, mixing the extended-life calcium aluminophosphate cement composition with a cement set activator to form an activated extended-life calcium aluminophosphate cement composition; introducing the activated extended-life calcium aluminophosphate cement composition into a subterranean formation; and allowing the activated extended-life calcium aluminophosphate cement composition to set in the subterranean formation.
 2. The method of claim 1, wherein the cement set retarder is selected from the group consisting of hydroxycarboxylic acids or their respective salts, boric acid or its respective salt, and any combination thereof.
 3. The method of claim 1, wherein the cement set retarder is present in an amount of about 6% to about 8% by weight of the extended-life calcium aluminophosphate cement composition.
 4. The method of claim 1, wherein the polyphosphate comprises sodium hexametaphosphate.
 5. The method of claim 1, wherein the polyphosphate is present in an amount of about 1% to about 30% by weight of the extended-life calcium aluminophosphate cement composition.
 6. The method of claim 1, wherein the cement set activator is selected from the group consisting of Groups IA and IIA hydroxides, alkaline aluminates, Portland cement; and wherein the cement set activator is present in an amount of about 0.01% to about 10% by weight of the extended-life calcium aluminophosphate cement composition.
 7. The method of claim 1, wherein the extended-life calcium aluminophosphate cement composition further comprises at least one lithium salt selected from the group consisting of lithium sulfate, lithium carbonate, and any combination thereof.
 8. The method of claim 1 wherein the extended-life calcium aluminophosphate cement composition is stored for a time period of at least about 7 days or longer.
 9. The method of claim 1, wherein the subterranean formation has a temperature of about 400° F. or more.
 10. An extended-life calcium aluminophosphate cement composition comprising: a calcium aluminate cement, wherein the calcium aluminate cement is present in an amount of about 40% to about 70% by weight of the extended-life calcium aluminophosphate cement composition, a polyphosphate, water, a cement set retarder, wherein the cement set retarder is present in an amount of about 6% to about 10% by weight of the extended-life calcium aluminophosphate cement composition, and aluminosilicate, wherein the aluminosilicate is present in an amount of about 1% to about 69% by weight of the extended-life calcium aluminophosphate cement composition, wherein the extended-life calcium aluminophosphate cement composition is free of cement kiln dust, and wherein the composition is capable of remining a pumpable fluid state for at least a period of about 1 day or longer.
 11. The composition of claim 10, wherein the cement set retarder is selected from the group consisting of hydroxycarboxylic acids or their respective salts, boric acid or its respective salt, and any combination thereof; wherein the cement set retarder is present in an amount of about 6% to about 8% by weight of the extended-life calcium aluminophosphate cement composition.
 12. The composition of claim 10, wherein the polyphosphate comprises sodium hexametaphosphate.
 13. The composition of claim 10, wherein the polyphosphate is present in an amount of about 1% to about 30% by weight of the extended-life calcium aluminophosphate cement composition.
 14. The composition of claim 10, wherein the composition further comprises a cement set activator; wherein the cement set activator is selected from the group consisting of Groups IA and IIA hydroxides, alkaline aluminates, Portland cement; and wherein the cement set activator is present in an amount of about 0.01% to about 10% by weight of the extended-life calcium aluminophosphate cement composition.
 15. A system for cementing a subterranean formation comprising: an extended-life calcium aluminophosphate cement composition comprising: a calcium aluminate cement, wherein the calcium aluminate cement is present in an amount of about 40% to about 70% by weight of the extended-life calcium aluminophosphate cement composition; a polyphosphate; water; a cement set retarder, wherein the cement set retarder is present in an amount of about 6% to about 10% by weight of the extended-life calcium aluminophosphate cement composition; aluminosilicate, wherein the aluminosilicate is present in an amount of about 1% to about 69% by weight of the extended-life calcium aluminophosphate cement composition, and wherein the extended-life calcium aluminophosphate cement composition is free of cement kiln dust; mixing equipment capable, wherein the cement set retarder is present in an amount of about 5% to about 10% by weight of the extended-life calcium aluminophosphate cement composition of mixing the extended-life calcium aluminophosphate cement composition; and pumping equipment capable of pumping the extended-life calcium aluminophosphate cement composition through a conduit and into a wellbore annulus that is penetrating the subterranean formation.
 16. The system of claim 15, further comprising a vessel capable of storing the extended-life calcium aluminophosphate cement composition for a time period of at least about 7 days or longer without setting.
 17. The system of claim 15, wherein the extended-life calcium aluminophosphate cement composition further comprises a cement set activator. 